Cementing HTHP Fluid Loss Control KOL FIL 33 CEM
- Property:It’s formed by the polymerization of the modified AMPS, low molecular weight amides, carboxyl acid.
We're here to help: Easy ways to get the answers you need.
PDF Download►Property
It’s formed by the polymerization of the modified AMPS, low molecular weight amides, carboxyl acid. It is soluble polymer that consists of more functional groups has better anti-temperature and anti-salt ability.
► Function
Temperature range :30~200℃
Salt range: fresh to saturated water
Filtration property: ＜100ml API FL
Solubility: full soluble
Compatibility: good
Solubility with cement: any cement classes
Stability: free water approach zero
Thickening time : thickening curve approach a right-angle
Density range : any density of cement slurry
Having a little retarder effect to the cement slurry.
Dosage: 1~3%(BWOC)
►Storage & package
Packaging and transport Sacked with three packages, 25kg/sack. Be kept away from moisture and possible damage of the packages in transportation. Stored in cool and dry situation and storage life is two years.
|
Items |
Specification |
|
Appearance |
Flowing powder or particles |
|
Initial consistency , BC |
≤30 |
|
Fluid loss,ml/80℃,6.9MPa,30min |
≤100 |
|
Thickening time ,ml/80℃,40MPa,40min |
≥60 |
|
Compression strength ,MPa/80℃. 21MPa. 24h |
≥14 |
|
residue(0.420mm screen) |
≤7% |
The ingredient of the cement in the table is : Jia hua class G cement , water quality: tap-water, W/C :0.44，Dosage of KOL-FIL CEM.: 1.5%(BWOC).